Material Supply: |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
EN Grade |
Chemical Component % |
||||||||||
|
C |
Cr |
Ni |
Mn |
P |
S |
Mo |
Si |
Cu |
N |
Other |
||
|
201 |
|
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50－7.50 |
≤0.060 |
≤0.030 |
- |
≤1.00 |
- |
≤0.25 |
- |
|
301 |
1.4310 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤1.00 |
- |
0.1 |
- |
|
304 |
1.4301 |
≤0.08 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
304L |
1.4307 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
304H |
1.4948 |
0.04~0.10 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
309S |
1.4828 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
309H |
|
0.04~0.10 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
310S |
1.4842 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤1.5 |
- |
- |
- |
|
310H |
1.4821 |
0.04~0.10 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤1.5 |
- |
- |
- |
|
316 |
1.4401 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
- |
- |
- |
|
316L |
1.4404 |
≤0.030 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
- |
- |
- |
|
316H |
|
0.04~0.10 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
- |
0.10-0.22 |
- |
|
316Ti |
1.4571 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
≤0.045 |
≤0.030 |
2.00-3.00 |
≤0.75 |
- |
- |
Ti5(C+N)~0.7 |
|
317L |
1.4438 |
≤0.03 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.045 |
≤0.030 |
3.00-4.00 |
≤0.75 |
- |
0.1 |
- |
|
321 |
1.4541 |
≤0.08 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
0.1 |
Ti5(C+N)~0.7 |
|
321H |
1.494 |
0.04~0.10 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
0.1 |
Ti4(C+N)~0.7 |
|
347 |
1.4550 |
≤0.08 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
Nb≥10*C%-1.0 |
|
347H |
1.4942 |
0.04~0.10 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
≤0.045 |
≤0.030 |
- |
≤0.75 |
- |
- |
Nb≥8*C%-1.0 |
|
409 |
S40900 |
≤0.03 |
10.50-11.70 |
0.5 |
≤1.00 |
≤0.040 |
≤0.020 |
- |
≤1.00 |
- |
0.03 |
Ti6(C+N)-0.5 Nb0.17 |
|
430 |
S43000 |
≤0.12 |
16.00-18.00 |
0.75 |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
436 |
S43600 |
≤0.025 |
16.00-19.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
0.75-1.0 |
≤1.00 |
|
≤0.025 |
Nb+Ti:8(C+N)~0.80 |
|
439 |
S43035 |
≤0.030 |
17.50-18.50 |
- |
≤1.00 |
≤0.040 |
≤0.015 |
- |
≤1.00 |
- |
≤0.030 |
Ti+Nb:0.2+4C~0.75 |
|
441 |
S44100 |
≤0.030 |
17.50-18.50 |
- |
≤1.00 |
≤0.040 |
≤0.015 |
- |
≤1.00 |
- |
≤0.030 |
Ti:0.1-0.6 Nb:3C+0.3~1.0 |
|
442 |
S44200 |
≤0.025 |
18.0-23.0 |
- |
≤1.00 |
≤0.040 |
≤0.035 |
- |
≤1.00 |
- |
|
|
|
443 |
S44300 |
≤0.025 |
19.5-22.0 |
- |
≤1.00 |
≤0.035 |
≤0.015 |
- |
≤1.00 |
- |
≤0.025 |
Nb+Ti:0.2+4(C+N)~0.75 |
|
444 |
S44400 |
≤0.025 |
17.00-20.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
1.75-2.5 |
≤1.00 |
|
≤0.035 |
Ti+Nb:0.2+4(C+N)~0.8 |
|
446 |
S44600 |
≤0.2 |
23.0-27.0 |
0.75 |
≤1.50 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
|
0.25 |
|
|
410 |
1Cr13 |
0.08~0.15 |
11.50-13.50 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
410J1 |
1Cr13Mo |
0.08-0.18 |
11.50-14.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
0.30-0.60 |
≤1.00 |
- |
- |
- |
|
420 |
2Cr13 |
≥0.15 |
12.00-14.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
420J2 |
3Cr13 |
0.26-0.35 |
12.00-14.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
|
4Cr13 |
0.36-0.45 |
12.00-14.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
431 |
1Cr17Ni2 |
≤0.2 |
15.00-17.00 |
1.25-2.50 |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
440C |
11Cr17 |
0.95-1.20 |
16.00-18.00 |
- |
≤1.00 |
≤0.040 |
≤0.030 |
0.75 |
≤1.00 |
- |
- |
- |
|
17-4PH |
630/1.4542 |
≤0.07 |
15.50-17.50 |
3.00-5.00 |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
3.00-5.00 |
- |
Nb+Ta:0.15-0.45 |
|
17-7PH |
631 |
≤0.09 |
16.00-18.00 |
6.50-7.50 |
≤1.00 |
≤0.040 |
≤0.030 |
- |
≤1.00 |
- |
- |
Al 0.75-1.50 |
|
Cold-rolled Sheet Thickness： 0.1mm-5mm Width: 1000/1219/1500/2000mm |
2B |
After cold rolled,the products are treated by heattreatment,pickling or similiar methods,skin passing to obtain proper surface brightness. |
|
2D |
After cold rolled,the products are treated by heattreatment,pickling or similiar methods,skin passing with rough roll to obtain surface with certain roughness. |
|
|
HL |
Products are treated by polishing with proper abrasive substance to obtain continuous lines. |
|
|
No.4 |
Products are treated by polishing with proper abrasive substance(grain size 150-320)according to GB2477. |
|
|
BA |
After cold rolled,the products are treated by bright annealing method to obtain surface brightness. |
|
|
No.8 |
Products are treated by polishing with proper abrasive substance. The product have excellent brightness and prefer reflexivity can to be the mirror. |
|
|
Hot Rolled Plate |
No.1 |
After hot rolled,the products are treated by heattreatment,pickling or similiar methods,skin passing to obtain proper surface brightness. |
|
Stainless Steel Perforated Sheet |
depending on perforation |
Thickness:0.2 mm to 30mm Hole:0.25mm-200mm |
|
Decorative Sheet |
Width: 1000/1219/1500/2000mm/2500 |
Thickness: |
|
Checkered Plate |
Width: 1000/1219/1500/2000mm/2500 |
Thickness: |